Effects of acetylation and hydrothermal treatment on lignin as revealed by cellular UV -Spectroscopy in Norway Spruce (Picea abies [L.] Karst.)
The effect of two different wood modification treatments on the lignin of Norway spruce wood was studied by means of cellular UV-spectroscopy. The modification treatments chosen were acetylation using acetic anhydride and a two step hydrothermal treatment. Small cross sectional thin slides from the wood surface were taken and were subsequently analysed using a UV-micro-spectro-photometer. The modified samples were compared with a non-treated control sample. The results revealed changes in the absorption spectra of lignin after both modification treatments. Spectra of the compound middle lamella (CML) of acetylated wood revealed a decrease in the lignin-specific absorption maximum at 280nm, which is considered to be caused by superficial leaching of lignin due to acetylation. The retarding effect of acetylation on UV-degradation of wood is discussed. In hydrothermal-treated wood the 280nm maximum was increased within the S2 layer. This maximum remained almost unchanged in the CML while a lower maximum was observed at about 330nm. Changes in the chromophoric behaviour of lignin are probably caused by de-masking reactions within the S2 layer resulting from hydrolysis of carbohydrates and side chain reactions. Both treatments lead to a severe decrease in absorption at the lower end of the spectrum towards 250nm which is possibly attributed to changes or even splitting of biphenyls
Dateien
Zitieren
Zugriffsstatistik
Rechte
Nutzung und Vervielfältigung:
Alle Rechte vorbehalten